NOVOTEST Leeb C 动态里氏探头 (370~1740 MPa)

Application: Surface-hardened components, coatings, thin-walled or impact-sensitive parts

Application: Surface hardened components, coatings, thin walled or impact sensitive components (small measuring indentation)

Indenter type: Tungsten carbide

Test object requirements

Minimum sample weight:

Without support: 1.5 kg (3.3 lbs).

With support: 0.5 kg (1.1 lbs).

Coupled: 0.02 kg (0.045 lbs).

Minimum sample thickness:

Uncoupled: 15 mm (0.59 inch).

Coupled: 1 mm (0.04 inch).

Surface layer thickness: 0.8 mm (0.03 inch).

Material: low, fine and medium grained ferrous and non-ferrous metals

Measuring range

HLC: 300~800

HRC: 20~70

HB: 90~650

HV:230~940

Tensile strength, MPa: 370~1740

User calibrations for any range (for example: HV10-1000)

Measurement accuracy

HLC: ±4

HRC: ±2

HB: ±10

HV: ±15

Scales

Precalibrated for HRC, HRA, HRB, HB, HV, MPA

Can be calibrated for any other (Shore HS, etc.)

Materials

Precalibrated for steel, alloy steel, cast iron, stainless steel, aluminum, bronze, brass, copper

Can be calibrated for any other

Standard:ASTM A956

Compatible models:T-UD3 (Lab), T-D3 (Lab), T-UD2 (Lab), T-D2 (Lab)

Operating environment

Temperature: -20°C ~ 50°C

Humidity: 30% ~ 80% R.H

Weight (with cable), g:95

Dimensions, mm:141*20